|IS 814:2004 –||EB 5426 H3 JX|
|AWS 5.1 –||E 7018|
WELDMETAL – 7018 is a basic coated, Iron powder low Hydrogen electrodes, Specially design for welding of medium-high
tensile steels with RADIOGRAPHIC quality welds metals, weld metal recovery is min. 110%. Weld metal has an excellent
ductility and notch toughness down to minus 30°C which is the greater and the special characteristic of weld metal-7018
electrodes, Typical hydrogen content is 5ml/100 gms of weld metal deposit cause to save the cracked from weld metal &
provide the good strength of the job.
WELDMETAL- 7018, is best to weld the following as : Storage Tank, Blast furnace Shells, Pressure Vessels, Railway Wagons,
Penstocks pipelines, Boilers, Dynamic loading structures, harden able low alloy steel, equipment subjected to High Stress
and Dynamic Loading, equipment requires having impact at minus -45°C, thick & heavy plates of carbon & High Tensile steels.
1.20 – 1.60
|Yield strength||Ultimate Tensile Strength||Elongation%||CVN Impact at – 30°C|
360N /mm2 min
510 -650 N /mm2
26% on 5d min
30 joules min
To obtain the best result, use welding current within the recommended range, RE-DRY the electrodes at 350°C for one hour or at 250°C for two hours,
use directly from the oven, store the electrodes in Dry Place.
2.50x350MM, 3.15x350MM, 4x350MM